NANOGOLD® PRODUCT INFORMATION

Nanogold® Gold-Antibody Conjugates
[Nanogold® Gold-Antibody Conjugates product page]

Technical Assistance Online
  Instructions (PDF)
  Material Safety Data Sheet (PDF)

Contents

• Product Information
• General Considerations for Immunostaining with NANOGOLD® Reagents
• Using Stains with NANOGOLD®
• Temperature Caution
• Thiol Caution
• Electron Microscopy Immunolabeling with NANOGOLD®
  1. Cells in Suspension
  2. Thin Sections
• Special Considerations for Viewing NANOGOLD® in the Electron Microscope
• Silver Enhancement of NANOGOLD® for EM
• Immunolabeling and Silver Enhancement with NANOGOLD® for Light Microscopy
• Immunoblotting
• References

Warning: For research use only. Not recommended or intended for diagnosis of disease in humans or animals. Do not use internally or externally in humans or animals. Non radioactive and non carcinogenic.

Product Information

Contents

General Considerations for Immunostaining with Nanogold® Reagents

The major difference will be in the results:

• NANOGOLD® is an extremely uniform 1.4 nm diameter gold particle (ca.10%).

• NANOGOLD® conjugates contain absolutely no aggregates. This is in sharp contrast to other colloidal gold conjugates that usually are prepared by centrifugation to remove the largest aggregates and frequently contain smaller aggregates.

• Close to 1 NANOGOLD® particle to 1 Fab (or IgG) make this product distinct from the 0.2 - 10 variable stoichiometry of other colloidal gold antibody preparations.

• NANOGOLD® particles do not have affinity to proteins as do other other colloidal golds. This reduces background and false labeling.

• NANOGOLD® develops better with silver than do most other colloidal golds giving it higher sensitivity. Silver enhancement can be used for light microscopy and immunoblotting with improved results.

Using Stains with Nanogold®

1. Use of reduced amounts or concentrations of usual stains.
2. Use of lower atomic number stains such as NANOVAN, a Vanadium based stain.²
3. Enhancement of NANOGOLD® with silver developers, such as LI SILVER or HQ SILVER.

Temperature Caution

Thiol Caution

Contents

Electron Microscopy Immunolabeling with Nanogold®

Cells in Suspension

1. Optional fixing of cells: e.g., with glutaraldehyde (0.05 - 1% for 15 minutes) in PBS. Do not use Tris buffer since this contains an amine. After fixation, centrifuge cells (e.g. 1 ml at 10,000,000 cells/ml) at 300 X g, 5 minutes; discard supernatant; resuspend in 1 ml buffer. Repeat this washing (centrifugation and resuspension) 2 times.
2. Incubate cells with 0.02 M glycine in PBS (5 mins). Centrifuge, then resuspend cells in PBS-BSA buffer (specified below) for 5 minutes.
3. Place 50 - 200 microliters of cells into Eppendorf tube and add 5 - 10 microliters of primary antibody (or antiserum). Incubate 30 minutes with occasional shaking (do not create bubbles which will denature proteins).
4. Wash cells using PBS-BSA as described in step 1 (2 X 5 mins). Resuspend in 1 ml Buffer 1.
5. Dilute NANOGOLD® ~ 50 times in PBS-BSA buffer and add 30 mmicoliters to cells; incubate for 30 minutes with occasional shaking.
6. Wash cells in PBS-BSA as described in step 1 (2 X 5 mins).
7. Fix cells and antibodies using a final concentration of 1% glutaraldehyde in PBS for 15 minutes. Then remove fixative by washing with buffer 1 (3 X 5 mins).

Negative staining may be used for electron microscopy of small structures or single molecules which are not embedded. Negative stain must be applied after the silver enhancement. NANOVAN negative stain is specially formulated for use with NANOGOLD® reagents; it is based on vanadium, which gives a lighter stain than uranium, lead or tungsten-based negative stains and allows easier visualization of NANOGOLD® particles with little or no silver enhancement.²

Thin Sections

Labeling with NANOGOLD® may be performed before or after embedding. ^5,6 Labeling before embedding and sectioning (the pre-embedding method) ^5,6 is used for the study of surface antigens, particularly small organisms such as viruses budding from host cells. It gives good preservation of cellular structure, and subsequent staining usually produces high contrast for study of the cellular details. Labeling after embedding and sectioning (the post-embedding method) ^5,6 allows the antibody access to the interior of the cells, and is used to label both exterior and interior features. The procedures for both methods are described below.

Thin sections mounted on grids are floated on drops of solutions on parafilm or in well plates. Hydrophobic resins usually require pre-etching.

PROCEDURE FOR PRE-EMBEDDING METHOD:⁵

1. Float on a drop of water for 5 - 10 minutes.
2. Incubate cells with 1 % bovine serum albumin in PBS buffer at pH 7.4 for 5 minutes; this blocks any non-specific protein binding sites and minimizes non-specific antibody binding.
3. Incubate with primary antibody, diluted at usual working concentration in PBS-BSA (30 mins - 1 hour, or usual time. Buffer formulations are given overleaf)
4. Rinse with PBS-BSA (3 X 1 min).
5. Incubate with NANOGOLD® reagent diluted 1/40 - 1/200 in PBS-BSA with 1 % normal serum from the same species as the NANOGOLD® reagent, for 10 minutes to 1 hour at room temperature.
6. Rinse with PBS-BSA (3 X 1 min), then PBS (3 X 1 min).
7. Postfix with 1 % glutaraldehyde in PBS (10 mins).
8. Rinse in deionized water (2 X 5 min).
9. Dehydrate and embed according to usual procedure. Use of a low-temperature resin (eg. Lowicryl) is recommended; if higher temperature embedding resins are used, silver enhancement should be performed before embedding.
10. Stain (uranyl acetate, lead citrate or other positive staining reagent) as usual before examination.

PROCEDURE FOR POST-EMBEDDING METHOD:⁵

1. Prepare sections on plastic or carbon-coated nickel grid. Float on a drop of water for 5 - 10 minutes.
2. Incubate with 1 % solution of bovine serum albumin in PBS buffer at pH 7.4 for 5 minutes to block non-specific protein binding sites.
3. Incubate with primary antibody, diluted at usual working concentration in PBS-BSA (1 hour or usual time. Buffer formulations are given overleaf)
4. Rinse with PBS-BSA (3 X 1 min).
5. Incubate with NANOGOLD® reagent diluted 1/40 - 1/200 in PBS-BSA with 1 % normal serum from the same species as the NANOGOLD® reagent, for 10 minutes to 1 hour at room temperature.
6. Rinse with PBS (3 X 1 min).
7. Postfix with 1 % glutaraldehyde in PBS at room temperature (3 mins).
8. Rinse in deionized water for (2 X 5 min).
9. If desired, contrast sections with uranyl acetate and/or lead citrate before examination.

Silver enhancement may also be used to render the NANOGOLD® particles more easily visible (see below); this is recommended if stains such as uranyl acetate or lead citrate are applied. Silver enhancement should be completed before these stains are applied.

Contents

Special Considerations for Direct Viewing of Nanogold® in the Electron Microscope

NANOGOLD® provides a much improved resolution and smaller probe size over other colloidal gold antibody products. However, because NANOGOLD® is only 1.4 nm in diameter, it will not only be smaller, but will appear less intense than, for example, a 5 nm gold particle. With careful work, however, NANOGOLD® may be seen directly through the binoculars of a standard EM even in 80 nm thin sections. However, achieving the high resolution necessary for this work may require new demands on your equipment and technique. Several suggestions follow:

1. Before you start a project with NANOGOLD® it is helpful to see it so you know what to look for. Dilute the NANOGOLD® stock 1:5 and apply 4 ml to a grid for 1 minute. Wick the drop and wash with deionized water 4 times.

2. View NANOGOLD® at 100,000 X magnification with 10 X binoculars for a final magnification of 1,000,000 X. Turn the emission up full and adjust the condenser for maximum illumination.

3. The alignment of the microscope should be in order to give 0.3 nm resolution. Although the scope should be well aligned, you may be able to skip this step if you do step

4. Objective stigmators must be optimally set at 100,000 X. Even if the rest of the microscope optics are not perfectly aligned, adjustment of the objective stigmators may compensate and give the required resolution. You may want to follow your local protocol for this alignment but since it is important, a brief protocol is given here:
   1. At 100,000 X (1 X 10⁶ with binoculars), over focus, under focus, then set the objective lens to in focus. This is where there is the least amount of detail seen.
   2. Adjust each objective stigmator to give the least amount of detail in the image.
   3. Repeat steps a and b until the in focus image contains virtually no contrast, no wormy details, and gives a flat featureless image.

5. Now underfocus slightly, move to a fresh area, and you should see small black dots of 1.4 nm size. This is the NANOGOLD®. For the 1:5 dilution suggested, there should be about 5 to 10 gold spots on the small viewing screen used with the binoculars. Contrast and visibility of the gold clusters is best at 0.2 - 0.5 m defocus, and is much worse at typical defocus values of 1.5 - 2.0 m commonly used for protein molecular imaging.

6. In order to operate at high magnification with high beam current, thin carbon film over fenestrated holey film is recommended. Alternatively, thin carbon or 0.2% Formvar over a 1000 mesh grid is acceptable. Many plastic supports are unstable under these conditions of high magnification/high beam current and carbon is therefore preferred. Contrast is best using thinner films and thinner sections.

7. Once you have seen NANOGOLD® you may now be able to reduce the beam current and obtain better images on film. For direct viewing with the binoculars reduction in magnification from 1,000,000 X to 50,000 X makes the NANOGOLD® much more difficult to observe and not all of the golds are discernable. At 30,000 X (300,000 X with 10 X binoculars) NANOGOLD® particles are not visible. It is recommended to view at 1,000,000 X, with maximum beam current, align the objective stigmators, and then move to a fresh area, reduce the beam, and record on film.

8. If the demands of high resolution are too taxing or your sample has an interfering stain, a very good result may be obtained using silver enhancement to give particles easily seen at lower magnification.

Silver Enhancement of Nanogold® for EM

Our LI SILVER silver enhancement system is convenient and not light sensitive, and suitable for all applications. Improved results in the EM may be obtained using HQ SILVER, which is formulated to give more controllable particle growth and uniform particle size distribution,⁷ at neutral pH for best possible ultrastructural preservation.

Specimens must be thoroughly rinsed with deionized water before silver enhancement reagents are applied. This is because the buffers used for antibody incubations and washes contain chloride ions and other anions which form insoluble precipitates with silver. These are often light-sensitive and will give non-specific staining. To prepare the developer, mix equal amounts of the enhancer and initiator immediately before use. NANOGOLD® will nucleate silver deposition resulting in a dense particle 2-20 nm in size or larger depending on development time. Use nickel grids (not copper).

The relevent procedure for immunolabeling should be followed up to step 7 as described above. Silver enhancement is then performed as follows:

1. Rinse with deionized water (2 X 5 mins).
2. OPTIONAL (may reduce background): Rinse with 0.02 M sodium citrate buffer, pH 7.0 (3 X 5 mins).
3. Float grid with specimen on freshly mixed developer for 1-8 minutes, or as directed in the instructions for the silver reagent. More or less time can be used to control particle size. A series of different development times should be tried, to find the optimum time for your experiment. With HQ silver, a development time of 4 min. gives 15-40 nm round particles.
4. Rinse with deionized water (3 X 1 min).
5. Mount and stain as usual.

NOTE: Treatment with osmium tetroxide followed by uranyl acetate staining can lead to much more drastic loss of the silver enhanced NANOGOLD® particles. This may be prevented by gold toning:⁸

1. After silver enhancement, wash thoroughly with dionized water.
2. 0.05 % gold chloride: 10 minutes at 4°C.
3. Wash with deionized water.
4. 0.5 % oxalic acid: 2 mins at room temperature.
5. 1 % sodium thiosulfate (freshly made) for 1 hour.
6. Wash thoroughly with deionized water and embed according to usual procedure.

Contents

Immunolabeling and Silver Enhancement with Nanogold® for Light Microscopy

Samples must be rinsed with deionized water before silver enhancement. This is because the reagent contains silver ions in solution, which react to form a precipitate with chloride, phosphate and other anions which are components of buffer solutions. The procedure for immunolabeling with NANOGOLD® and silver enhancement is given below.

1. Spin cells onto slides using Cytospin, or use parafin section.
2. Incubate with 1 % solution of bovine serum albumin in PBS (PBS-BSA) for 10 minutes to block non-specific protein binding sites.
3. Incubate with primary antibody, diluted at usual working concentration in PBS-BSA (1 hour or usual time)
4. Rinse with PBS-BSA (3 X 2 min).
5. Incubate with NANOGOLD® reagent diluted 1/40 - 1/200 in PBS-BSA with 1 % normal serum from the same species as the NANOGOLD® reagent, for 1 hour at room temperature.
6. Rinse with PBS (3 X 5 min).
7. Postfix with 1 % glutaraldehyde in PBS at room temperature (3 mins).
8. Rinse with deionized water (3 X 1 min).
9. OPTIONAL (may reduce background): Rinse with 0.02 M sodium citrate buffer, pH 7.0 (3 X 5 mins).
10. Develop specimen with freshly mixed developer for 5-20 minutes, or as directed in the instructions for the silver reagent. More or less time can be used to control intensity of signal. A series of different development times may be used, to find the optimum enhancement for your experiment; generally a shorter antibody incubation time will require a longer silver development time.
11. Rinse with deionized water (2 X 5 mins).
12. The specimen may now be stained if desired before examination, with usual reagents.

To obtain an especially dark silver signal, the silver enhancement may be repeated with a freshly mixed portion of developer.

Contents

Immunoblotting

1. Spot 1 microliter dilutions of the antigen in buffer 4 onto hydrated nitrocellulose membrane. Use an antigen concentration range from 100 ng to 0.01 pg / microliter.
2. Block with buffer 1 for 30 minutes at 37°C.
3. Incubate with primary antibody according to usual procedure (usually 1 or 2 hours).
4. Rinse with buffer 1 (3 X 10 mins).
5. Incubate with a 1/100 to 1/200 dilution of the NANOGOLD® reagent in buffer 2 for 2 hours at room temperature.
6. Rinse with buffer 3 (3 X 5 mins), then buffer 4 (2 X 5 mins).
7. OPTIONAL (may improve sensitivity): Postfix with glutaraldehyde, 1 % in buffer 4 (10 mins).
8. Rinse with deionized water (2 X 5 mins).
9. OPTIONAL (may reduce background): Rinse with 0.05 M EDTA at pH 4.5 (5 mins).
10. Develop with freshly mixed silver developer for 20-25 minutes or as directed in the instructions for the silver reagent, twice. Rinse thoroughly with deionized water between developments to remove all the reagent.
11. Rinse several times with deionized water.

Other procedures may be used; for example the NANOGOLD® reagent may be used as a tertiary labeled antibody, or a custom NANOGOLD® conjugate may be the primary antibody. If additional antibody incubation steps are used, rinse with buffer 3 (3 X 10 mins) after incubation.

Contents

References

1. Hainfeld, J. F., and Powell, R. D., Cell Vision, 4 308-324 (1997); Furuya, F. R., and Hainfeld, J. F., J. Histochem. Cytochem., 40, 177 (1992); Furuya, F. R., Hainfeld, J. F., and Powell, R. D., Proc. 49th Ann. Mtg., Electron.Micros. Soc. Amer.; Bailey, G. W. (Ed.), San Francisco Press, San Francisco, CA; 1991, p. 284.

2. Tracz, E., Dickson, D. W., Hainfeld, J. F., and Ksiezak-Reding, H. Brain Res., 773, 33-44 (1997); Gregori, L., Hainfeld, J. F., Simon, M. N., and Goldgaber, D. Binding of amyloid beta protein to the 20S proteasome. J. Biol. Chem., 272, 58-62 (1997); Hainfeld, J. F.; Safer, D.; Wall, J. S.; Simon, M. N.; Lin, B. J., and Powell, R. D.; Proc. 52nd Ann. Mtg., Micros. Soc. Amer.; G. W. Bailey and Garratt-Reed, A. J., (Eds.); San Francisco Press, San Francisco, CA, 1994, p. 132.

3. Hainfeld, J. F., and Furuya, F. R.; in Immunogold-Silver Staining: Principles, Methods and Applications (M. A. Hayat, Ed.), CRC Press, Boca raton, FL., 1995: pp. 71-96.

4. Krenács, T., and Krenács, L.; in Immunogold-Silver Staining: Principles, Methods and Applications (M. A. Hayat, Ed.), CRC Press, Boca raton, FL., 1995: pp. 57-69.

5. J. E. Beesley, in Colloidal Gold: Principles, Methods and Applications, M. A. Hayat, ed., Academic Press, New York, 1989; Vol. 1, pp. 421-425.

6. Lujan, R.; Nusser, Z.; Roberts, J. D. B.; Shigemoto R.; Ohishi, H., and Somogyi, P.: J. Chem. Neuroanat., 13, 219-241 (1997).

7. Humbel, B. M.; Sibon, O. C. M.; Stierhof, Y.-D., and Schwarz, H.: J. Histochem. Cytochem., 43, 735-737 (1995).

8. Arai, R., et al.; Brain Res. Bull. 28, 343-345 (1992).

9. Moeremans, M. et al., J. Immunol. Meth. 74, 353 (1984).

For a complete list of references citing this product, please visit our References page.

Contents